The production of Nd:Y2O3 transparent ceramics with its optical and structural properties. Iranian Journal of Ceramic Science & Engineering 2018; 7 (1) :37-51
URL: http://ijcse.ir/article-1-574-en.html
Abstract:   (3073 Views)
In this work, the nanoscale Y2O3 powder was prepared with Nd2O3 ion at 1, 1.5 and 2% mol by ball milling for 20 hours, the particle size decreased significantly to 92.3 nm. A transparent pure ceramic disc of pure Yttrium doped with neodymium, which is used as laser active medium in power lasers, was made by a plasma spark sintering with a heating rate of 100 °C/min at 1400 °C for 15 minutes at a pressure of 70 MPa.The sample of Nd:Y2O3 transparency ceramic disc was significantly increased at the wavelength of the lens. The highest transmittance of Nd:Y2O3 ceramic reached 83% at the wavelength of 5 μm for 2.5 mm thick,Which is very close to the value of the theory of yttria that has been dopped to neodymium.
Full-Text [PDF 1112 kb]   (710 Downloads)    
Type of Study: Research | Subject: Bioceramics
Received: 2018/09/24 | Accepted: 2018/09/24