The effect of TiO2 concentration on microstructure, corrosion behavior and wear behavior of Ni-P-W-TiO2 coating
Abstract:   (387 Views)
Nickel-phosphorus coatings (Ni-P) are widely used in industry due to their high hardness, corrosion resistance and very good mechanical and chemical properties. Oxide particles such as TiO2 can be used to increase the wear resistance of these coatings. In this study, the Ni-P-W-TiO2 composite coating was deposited on the AISI 304L steel substrate using the electroplating method. Electroplating was performed at concentrations of 10, 20, and 30 g/L TiO2, and the effect of TiO2 concentrations on the microstructure, corrosion behavior, and wear behavior was investigated. Coatings were characterized by scanning electron microscopy (SEM). In order to investigate corrosion resistance, potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) tests were used in 3.5% NaCl aqueous solution. A pin on disk test was used to test the wear resistance of uncoated and coated samples. Sample micro-hardness was also measured by the Vickers hardness test. Examination of the microstructure showed that the best TiO2 concentration for deposition was 20 g/L. The results of Tafel and electrochemical impedance spectroscopy tests were also consistent with microscopic images, and the results showed that the coating formed at concentration of 20 g/L had the highest corrosion resistance compared to other coated and non-coated samples. Also, the results of the wear test showed that increasing the TiO2 concentration increases the micro-hardness and wear resistance.
Keywords: Coating, TiO2, Potentiodynamic polarization, Electrochemical impedance spectroscopy, Wear resistance.
Full-Text [PDF 4153 kb]   (98 Downloads)    
Type of Study: Research | Subject: Tile, Porcelain, Glaze, Pigment and Ink
Received: 2021/07/10 | Revised: 2021/09/20 | Accepted: 2021/07/1 | Published: 2021/07/1
Add your comments about this article
Your username or Email:

CAPTCHA


XML   Persian Abstract   Print


Download citation:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:

The effect of TiO2 concentration on microstructure, corrosion behavior and wear behavior of Ni-P-W-TiO2 coating. Iranian Journal of Ceramic Science & Engineering. 2021; 10 (1) :25-43
URL: http://ijcse.ir/article-1-845-en.html


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.
Volume 10, Issue 1 (7-2021) Back to browse issues page
نشریه علم و مهندسی سرامیک Iranian Journal of Ceramic Science & Engineering
Persian site map - English site map - Created in 0.05 seconds with 29 queries by YEKTAWEB 4353