The thermal activation and investigation of the structural order of kaolinite in kaolin and ballclay. Iranian Journal of Ceramic Science & Engineering 2017; 5 (4) :1-12
URL: http://ijcse.ir/article-1-467-en.html
Abstract:   (4330 Views)
In this study, domestic and foreign kaolin and ballclay were selected for thermal activation and structural order studies. The calcination temperature 700°C for 3 hrs was selested. Kaolin conversion to metakaolin was investigated using; differential thermal analysis, theramal gravimetric (DTA/TG), x-ray diffraction( XRD) and fourier transorm infrared spectroscopy (FTIR). The degree of kaolinite dehydroxylation in kaolins and ballclays were also investigated using TGA analysis. The highest and lowest degree of hydroxylation after calcination was 90 and 60% Respectively under  the same calcination conditions. Based on DTA and FTIR results, the highest order was observed in foreign kaolin and the lowest order was seen in the domestic ballcaly.but order indexes related to XRD, was shown different results with above analysis.
Full-Text [PDF 1030 kb]   (2220 Downloads)    
Type of Study: Research | Subject: Bioceramics
Received: 2017/08/5 | Accepted: 2017/08/5

Add your comments about this article : Your username or Email:
CAPTCHA

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.