Iranian Journal of Ceramic Science & Engineering
Volume 7, Issue 4 (3-2019)
2019, 7(4): 1-20 |
Back to browse issues page
Download citation:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:
Effect of Graphene Oxide Nanoparticles Addition on Mechanical and Biological Properties of Calcium Phosphate Cement. Iranian Journal of Ceramic Science & Engineering 2019; 7 (4) :1-20
URL: http://ijcse.ir/article-1-650-en.html
URL: http://ijcse.ir/article-1-650-en.html
Abstract: (3788 Views)
In the present study, we have evaluated the effects of graphene oxide (GO) addition on the physical-mechanical-biological properties of calcium phosphate cement (CPC). The in vitro cellular responses of MG63 and in vivo tissue responses after the implantation of CPC/GO in parietal bone defects of wistar rats were also investigated.
The brushite calcium phosphate cements were prepared by mixing β-tricalcium phosphate [β-TCP, Ca3(PO4)2] and monocalcium phosphate monohydrate [MCPM, Ca(H2PO4)2. H2O]. Inclusion of GO at the concentration of 0, 0.5, 2 and 5 wt% resulted in marginal decrease in setting time and significantly enhanced the compressive strength. New Ca-deficient apatite layer was deposited on the composite surface after immersing in SBF for 7 and 14 days. Field emission scanning electron microscope (FESEM) images indicated that GO incorporated brushite cement facilitates cell adhesion. In addition, alkaline phosphatase (ALP) activity of cells was improved compared with the pure CPC. Histological evaluation analysis showed that CPC/GO enhanced the efficiency of new bone formation in comparison with CPC.
We concluded that CPC/GO can overcome the flaws of previously developed natural CPCs and be potential candidates as bone cements for clinical application of bone repair and regeneration.
KEYWORDS: calcium phosphate cement, graphene oxide, osteogenesis.
In the present study, we have evaluated the effects of graphene oxide (GO) addition on the physical-mechanical-biological properties of calcium phosphate cement (CPC). The in vitro cellular responses of MG63 and in vivo tissue responses after the implantation of CPC/GO in parietal bone defects of wistar rats were also investigated.
The brushite calcium phosphate cements were prepared by mixing β-tricalcium phosphate [β-TCP, Ca3(PO4)2] and monocalcium phosphate monohydrate [MCPM, Ca(H2PO4)2. H2O]. Inclusion of GO at the concentration of 0, 0.5, 2 and 5 wt% resulted in marginal decrease in setting time and significantly enhanced the compressive strength. New Ca-deficient apatite layer was deposited on the composite surface after immersing in SBF for 7 and 14 days. Field emission scanning electron microscope (FESEM) images indicated that GO incorporated brushite cement facilitates cell adhesion. In addition, alkaline phosphatase (ALP) activity of cells was improved compared with the pure CPC. Histological evaluation analysis showed that CPC/GO enhanced the efficiency of new bone formation in comparison with CPC.
We concluded that CPC/GO can overcome the flaws of previously developed natural CPCs and be potential candidates as bone cements for clinical application of bone repair and regeneration.
The brushite calcium phosphate cements were prepared by mixing β-tricalcium phosphate [β-TCP, Ca3(PO4)2] and monocalcium phosphate monohydrate [MCPM, Ca(H2PO4)2. H2O]. Inclusion of GO at the concentration of 0, 0.5, 2 and 5 wt% resulted in marginal decrease in setting time and significantly enhanced the compressive strength. New Ca-deficient apatite layer was deposited on the composite surface after immersing in SBF for 7 and 14 days. Field emission scanning electron microscope (FESEM) images indicated that GO incorporated brushite cement facilitates cell adhesion. In addition, alkaline phosphatase (ALP) activity of cells was improved compared with the pure CPC. Histological evaluation analysis showed that CPC/GO enhanced the efficiency of new bone formation in comparison with CPC.
We concluded that CPC/GO can overcome the flaws of previously developed natural CPCs and be potential candidates as bone cements for clinical application of bone repair and regeneration.
KEYWORDS: calcium phosphate cement, graphene oxide, osteogenesis.
In the present study, we have evaluated the effects of graphene oxide (GO) addition on the physical-mechanical-biological properties of calcium phosphate cement (CPC). The in vitro cellular responses of MG63 and in vivo tissue responses after the implantation of CPC/GO in parietal bone defects of wistar rats were also investigated.
The brushite calcium phosphate cements were prepared by mixing β-tricalcium phosphate [β-TCP, Ca3(PO4)2] and monocalcium phosphate monohydrate [MCPM, Ca(H2PO4)2. H2O]. Inclusion of GO at the concentration of 0, 0.5, 2 and 5 wt% resulted in marginal decrease in setting time and significantly enhanced the compressive strength. New Ca-deficient apatite layer was deposited on the composite surface after immersing in SBF for 7 and 14 days. Field emission scanning electron microscope (FESEM) images indicated that GO incorporated brushite cement facilitates cell adhesion. In addition, alkaline phosphatase (ALP) activity of cells was improved compared with the pure CPC. Histological evaluation analysis showed that CPC/GO enhanced the efficiency of new bone formation in comparison with CPC.
We concluded that CPC/GO can overcome the flaws of previously developed natural CPCs and be potential candidates as bone cements for clinical application of bone repair and regeneration.
| Rights and permissions | |
 |
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License. |